Thermodynamics of Molybdenum Trioxide Encapsulated in Zeolite Y
  • +10
  • Xianghui Zhang,
  • Andrew Strzelecki,
  • Cody Cockreham,
  • Vitaliy Goncharov,
  • Houqian Li,
  • Junming Sun,
  • Hui Sun,
  • Xiaofeng Guo,
  • Hongwu Xu,
  • Su Ha,
  • Baodong Wang,
  • Yong Wang,
  • Di Wu
Xianghui Zhang
Washington State University

Corresponding Author:[email protected]

Author Profile
Andrew Strzelecki
Washington State University
Cody Cockreham
Washington State University
Author Profile
Vitaliy Goncharov
Washington State University
Author Profile
Houqian Li
Washington State University
Author Profile
Junming Sun
Washington State University
Author Profile
Hui Sun
East China University of Science and Technology
Author Profile
Xiaofeng Guo
Washington State University
Author Profile
Hongwu Xu
Los Alamos National Laboratory
Author Profile
Su Ha
Washington State University
Author Profile
Baodong Wang
National Institute of Clean and Low Carbon Energy
Author Profile
Yong Wang
Washington State University
Author Profile
Di Wu
Washington State University
Author Profile

Abstract

Zeolites with encapsulated transition metal species are extensively applied in the chemical industry as heterogenous catalysts for favorable kinetic pathways. To elucidate the energetic insights into formation of subnano-sized molybdenum trioxide (MoO3) encapsulated/confined in zeolite Y (FAU) from constituent oxides, we performed a systematic experimental thermodynamic study using high temperature oxide melt solution calorimetry as the major tool. Specifically, the formation enthalpy of each MoO3/FAU is less endothermic than corresponding zeolite Y, suggesting enhanced thermodynamic stability. As Si/Al ratio increases, the enthalpies of formation of MoO3/FAU with identical loading (5 Mo-wt%) tend to be less endothermic, ranging from 61.1 ± 1.8 (Si/Al = 2.9) to 32.8 ± 1.4 kJ/mol TO2 (Si/Al = 45.6). Coupled with spectroscopic, structural and morphological characterizations, we revealed intricate energetics of MoO3 – zeolite Y guest – host interactions likely determined by the subtle redox and/or phase evolutions of encapsulated MoO3.
17 May 2021Submitted to AIChE Journal
19 May 2021Submission Checks Completed
19 May 2021Assigned to Editor
26 May 2021Reviewer(s) Assigned
28 Jun 2021Editorial Decision: Revise Major
13 Aug 20211st Revision Received
16 Aug 2021Submission Checks Completed
16 Aug 2021Assigned to Editor
18 Aug 2021Reviewer(s) Assigned
09 Sep 2021Editorial Decision: Accept
Dec 2021Published in AIChE Journal volume 67 issue 12. 10.1002/aic.17464